Product Description

Low temperature and high temperature processing EVA film

1. High transparency: light transmittance ＞92.1%, Haze ＜0.3%

2. Wide range of adhesion: processing temperature between 80-130℃ provide good adhesive strength

3. Excellent UV blocking, to resist 99% UV, ensuring the safety of indoor environment.

4. Mobility, easy to fill in concave space, ideal choice for fabric and other insertion materials.

 

For this kind of EVA film, it can process at 80 degree for decorative fabric/paper laminating, especially

 for the PDLC film laminating.

Below is the processing data for the smart switchable glass laminating.

EVATREND 80-130(0.38mm) Low Temperature-High Temperature High Transparent Film

Low temperature process parameter(80 degree)

glass thickness (mm)	60℃ low temperature hold time	80℃ high  temperature hold time	Middle  temperature℃	Middle  temperature hold time	Pressure range
4+4mm	25 minute	65 minute	80℃	5 minute	0.02-0.04
5+5mm	25 minute	70 minute	80℃	8 minute	0.02-0.04
6+6mm	25 minute	75 minute	80℃	12 minute	0.02-0.04
8+8mm	25 minute	80 minute	80℃	15 minute	0.02-0.04
10+10mm	25 minute	90 minute	80℃	20 minute	0.02-0.04

High temperature process parameter(130 degree)

glass thickness (mm)	60℃ low temperature hold time	130  high  temperature hold time	Middle  temperature℃	Middle  temperature hold time	Pressure range
4+4mm	25 minute	40 minute	110℃	5 minute	0.02-0.04
5+5mm	25 minute	45 minute	110℃	8 minute	0.02-0.04
6+6mm	25 minute	50 minute	110℃	12 minute	0.02-0.04
8+8mm	25 minute	60 minute	110℃	15 minute	0.02-0.04
10+10mm	25 minute	70 minute	110℃	20 minute	0.02-0.04

Note: In low temperature process, it is better for fabric laminated glass, cause some insert materials can not

 stand very high temperature. But if make transparent laminated glass, we suggest use high temperature process.